Metastable paramagnetic face-centered cubic (fcc) Fe films grown on a Cu(100) single crystal at room temperature can be transformed to the ferromagnetic body-centered cubic (bcc) structure by ion irradiation. We have employed this technique to write small ferromagnetic patches by Ar+ irradiation through a gold coated SiN mask with regularly arranged 80-nm diameter holes, which was placed on top of the as-prepared fcc Fe films. Nanopatterning was performed on both 8-monolayer (ML) Fe films grown in ultrahigh vacuum as well as 22-ML films stabilized by dosing carbon monoxide during growth. The structural transformation of these nano-patterned films was investigated using scanning tunneling microscopy. In both 8 and 22-ML fcc Fe films, the bcc needles are found to protrude laterally out of the irradiated part of the sample, limiting the resolution of the technique to a few 10 nm. The magnetic transformation was confirmed by magnetic force microscopy.
Corresponding author: M. Schmid (schmid).
Full text (PDF) copyright (2011) American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics.